Compare products with technical highlights, document cues, and product details.
TiB2 - Nanopowder Purity: > 98,5% Particle size: D90 < 1μm Controlled admixtures, %: B2O3 < 0,1; C < 0,3; Fe < 0,1; Si < 0,2.
TiB2 / B4C / W2B5 (30 / 10 / 60)- Nanopowder mixture Composition: W2B5 > 59,4%; TiB2 > 29,5%; B4C > 9,6% Controlled admixtures, %: B2O3 < 0,11; C < 0,45; Fe < 0,1; Si < 0,15.
Average particle size: 4-8 nm. Anatase phase. Stabilized by benzoic acid. Forms transparent colloidal solutions in MEK (methylethylketone) and many epoxides. Supplied as a 100 g/L solution in MEK.
Photocatalytic standard P25. Dry Nanopowder. Mixed rutile / anatase phase Average primary particle size: 21±5 nm. Specific surface: 50±10 m2/g; Purity after ignition: >99,5% Ignition loss: < 2%; Moisture: < 1,5% Al2O3 < 0,3 wt.%; SiO2 < 0,2 wt.% Tapped density: ca. 130 g/L.
Dry Nanopowder. Mixed rutile / anatase phase, treated with octylsilane Average primary particle size: 21±5 nm Specific surface: 45±10 m2/g Purity after ignition: TiO2 > 97%; SiO2 < 2,5 wt.% Ignition loss: < 5%; Moisture: < 1% C < 3,8 wt.%; Tapped density: ca. 200 g/L.
Produced by chemical synthesis Average particle size: 4-8 nm Loss on thempering (800 oC, 2 h): ca. 32% Dry nanopowder, free of organic stabilizers. Easily forms colloidal solutions in water.
Average particle size: 4-8 nm. Anatase phase. Stabilized by dodecylphosphonic acid and hexylamine. Forms transparent colloidal solutions in chloroform. Supplied as a powder.
Average particle size: 2±1 nm. Dry nanopowder. Readily forms colloidal solutions in water (up to 900g/L) and methanol.
Length: ca. 100 nm. Diameter: 20-40 nm Stabilized only with citrate. Phase: anatase Supplied as a 1 wt.% aqueous solution.
Length full range: 0,5-100 μm Diameter: 50-100 nm Phase: anatase Dry powder.
Produced by chemical synthesis Average particle size: 4-8 nm. Aqueous colloidal solutions: 5, 10 or 20 wt.%.
Produced by chemical synthesis Average particle size: 4-8 nm. Aqueous colloidal solutions: 5, 10 or 20 wt.%.
Average particle size: 2-5 nm. Mixed brookite / anatase phase Stabilized by tetramethylammonium hydroxide Aqueous colloidal solution, 20 wt.%.
Produced by chemical synthesis Average particle size: 4-8 nm. Aqueous colloidal solutions: 5, 10 or 20 wt.%.
Average particle size: 20±5 nm; Specific surface area: 80±5 m2/g X-ray analysis: cubic phase > 97% O < 3; C < 0,1; Fe < 0,02 Forms dark transparent stable colloidal suspensions in water.
Average particle size: 50±5 nm; Specific surface area: 22±5 m2 /g X-ray analysis: cubic phase > 99% Fe < 0,1; Si < 0,05; Ni < 0,1.
Purity 99,9% Average particle size: 100-200 nm (BET).
Average particles size: 30-50 nm Specific surface area: ca. 40 m²/g.
Large cavities (11.6 Å) connected by small windows (3.4 Å) Specific surface: ca. 1500 m2/g; Empirical Formula C8H10N4Co; Mw: 221,1.
Large cavities (11.6 Å) connected by small windows (3.4 Å) Specific surface: ca. 1600 m2/g, Empirical Formula C8H10N4Zn; Mw: 227,6.
Average particle size: ca. 14 nm; Specific surface area: 30±5 m2/g Purity: > 99%.
Average particle size: ca. 25 nm; Specific surface area: 19±5 m2/g Purity: > 99%.